Quick Look
| Density(g/cm³) | Tensile Strength | Young's Modulus | Elongation at Break | Glass Transition Temperature |
|---|---|---|---|---|
| 1.3 | 150MPa | 8000MPa | 1-3% | 50-70℃ |
About the Material
Advantages:
High Strength and Rigidity: Glass fiber reinforcement significantly improves tensile strength and stiffness, making it ideal for load-bearing applications.
Heat Resistance: Higher Heat Deflection Temperature (HDT) ~200-230°C (at 1.8 MPa) compared to standard Nylon 6,suitable for high-temperature environments.
Reduced Warping and Shrinkage: Glass fibers increase dimensional stability, reducing warping and shrinkage, which is common in unfilled Nylon 6, allows for more accurate and reliable prints.
Limitations:
Brittleness: Layer adhesion can be weaker due to fiber orientation.
Abrasive Nature: Glass fibers are highly abrasive, wearing out standard brass nozzles quickly.
Highly Hygroscopic: Must be dried at 80°C for 4-6 hours before printing to avoid print defects like bubbling or poor adhesion, storage in sealed containers with desiccant is necessary.
Chemical Composition Table for Black Nylon 6 Glass-filled
| Component | Composition |
| Nylon 6 | 70% |
| Glass Fiber | 30% |
| Colorant (Black) | Trace |
Mechanical Machining Properties Table for Black Nylon 6 Glass-filled
| Property | Value |
| Machinability Rating | Moderate |
| Cutting Speed (m/min) | 10~20 |
| Tool Wear Resistance | Low (due to abrasiveness) |
| Coolant Requirement | Essential |
| Surface Finish Quality | Moderate |
Design Parameters Table for SLS Printing with Black Nylon 6 Glass-filled
| Maximum Bulid Size（mm） | Minimum Wall Thickness | Minimum Drill Size | Minimum Assembly Gap | Tolerance |
| 380x380x420 | 0.8mm | 1mm | 0.2mm | 0.2%*L |
Industry Applications and Case Studies for SLS Printing with Black Nylon 6 Glass-filled
Aerospace and Aviation:
Application: Structural Aircraft Components,Drone Frames & UAV Components,Custom Jigs & Fixtures.
Case Study: A defense contractor developed printed UAV (drone) airframe components using Nylon 6 Glass-Filled, reducing the need for costly CNC machining while maintaining aerospace-grade strength.
Automotive:
Application:Engine Covers & Housings,Brackets & Mounting Fixtures,Dashboard Components.
Case Study: A leading automotive manufacturer used FDM-printed Nylon 6 GF for under-the-hood brackets, reducing weight while maintaining strength compared to metal alternatives.
Consumer Products:
Application:Ruggedized Electronic Casings,Custom Laptop Stands & Mounts,Drones & Camera Rigs.
Case Study: A consumer electronics company 3D printed custom mounting brackets for high-performance gaming laptops, ensuring heat resistance and lightweight support.
Frequently Asked Questions (FAQs) about SLS Printing with Black Nylon 6 Glass-filled
What are the benefits of using Black Nylon 6 Glass-filled in 3D printing?
Nylon 6 Glass-filled (Black) is an industrial-grade material that offers high strength, stiffness, and durability, making it ideal for functional and end-use parts.
Is Black Nylon 6 Glass-filled suitable for functional parts?
Yes, Nylon 6 Glass-filled (Black) is widely used in industrial applications where mechanical performance and reliability are crucial.
What industries benefit from SLS printing with Black Nylon 6 Glass-filled?
Industries such as automotive, aerospace, and consumer products benefit from the strength, dimensional stability, and visual appeal of Black Nylon 6 Glass-filled.
How accurate is SLS printing with Black Nylon 6 Glass-filled?
SLS printing with Black Nylon 12 Glass-filled can achieve tolerances of ±0.2 mm, which is suitable for most functional applications.
What post-processing is required for Black Nylon 6 Glass-filled-printed parts?
Post-processing may include bead blasting or polishing to improve the surface finish and appearance.
Can Black Nylon 6 Glass-filled be used in high-temperature environments?
Yes, Black Nylon 6 Glass-filled is well-suited for high-temperature applications due to its high heat resistance, structural stability, and low thermal expansion.
How strong are Black Nylon 6 Glass-filled-printed parts?
Black Nylon 6 Glass-filled is one of the strongest and stiffest materials available for 3D printing, it suitable for high-performance functional parts.